      幕墻鋁板變形問題核心介紹

      來源:http://www.mallhometrade.com  發布時間:2021-11-16 15:39:36  

      1、安裝版塊沒有邊肋與立肋,氣壓和氣體漲力下產生形變
      1. The installation plate has no side ribs and vertical ribs, and deformation occurs under air pressure and gas expansion
      這類形變狀況多發生在選用金屬復合板為設定的幕墻鋁板上。目前許多建筑小區業主為了更好地節約成本,采用不靠譜的生產商。生產廠家為獲較高盈利,版塊生產加工不安裝邊肋,中肋,只將鋁朔板疊成盒狀,立即用螺絲擰在架構上,版塊間隙抹膠密封性即使竣工。那樣幕墻鋁板的版塊抗壓強度達不上規定,版塊在正負極氣壓功效下造成向里向外的疲乏性撓度值形變,使表面規格提高。
      This kind of deformation mostly occurs on the curtain wall aluminum plate set with metal composite plate. At present, many building community owners adopt unreliable manufacturers in order to better save costs. In order to obtain higher profits, the manufacturer does not install side ribs and middle ribs in the production and processing of the plate. Only the aluminum plastic plate is stacked into a box shape, and immediately screw it on the structure with screws. The gap between the plates is coated with glue, and the sealing is even completed. In that way, the compressive strength of the plate of the curtain wall aluminum plate can not meet the requirements, and the plate will cause the fatigue deflection value deformation inward and outward under the effect of positive and negative pressure, so as to improve the surface specification.
      體現非常明顯的朝陽面的幕墻鋁板,因為施工技術是選用保溫暖墻的方式將版塊間隙所有用膠密封性嚴密,表面與構造墻間距里的氣體在陽光照射效用下提溫,版塊在氣體漲力功效下導致向外形變。
      The aluminum plate of curtain wall reflecting the very obvious sunrise surface, because the construction technology is to use the way of thermal insulation and warm wall to seal all the plate gaps tightly with glue. The gas in the distance between the surface and the structural wall increases the temperature under the effect of sunlight, and the plate changes to the shape under the effect of gas expansion.
      2、版塊與幕墻鋁板構造架構固定不動,內應力沒法放松造成形變
      2. The plate and the aluminum plate structure of the curtain wall are fixed, and the internal stress cannot be relaxed, resulting in deformation
      鋁合金板幕墻鋁板在時節氣溫差異比較大地域,在春初秋后溫度較低的時節,這時候的太陽光照射熱效率很強,尤其是色調較深的鋁合金板提溫比較大,鋁合金板在不一樣環境溫度下,每米長短上的熱變形值區別比較大。幕墻鋁板架構在里面,太陽危害較差,鋁合金板與架構較大時可造成80℃之上的溫度差,在鋁合金板規格過大時便會發生很大的線形澎漲差。假如幕墻鋁板版塊構造選用壓邊,將鋁合金板用螺絲固定不動在架構上的構造,將導致鋁合金板表面的內應力沒法釋放出來,驅使表面妥協,在氣體功效下向外發生形變狀況。

      鋁卷生產廠家
      Aluminum alloy plate curtain wall aluminum plate has large temperature difference in seasons. In the season of low temperature after early spring and autumn, the solar radiation thermal efficiency is very strong, especially the temperature rise of aluminum alloy plate with deep color is relatively large, and the thermal deformation value of aluminum alloy plate per meter is quite different under different ambient temperatures. The aluminum plate structure of curtain wall is inside, and the solar harm is poor. When the aluminum alloy plate and the structure are large, it can cause a temperature difference above 80 ℃, and a large linear surge difference will occur when the specification of aluminum alloy plate is too large. If the blank holder is selected for the structure of the aluminum plate plate of the curtain wall, and the aluminum alloy plate is fixed on the structure with screws, the internal stress on the surface of the aluminum alloy plate cannot be released, driving the surface to compromise and deform outward under the effect of gas.
      3、控制面板與邊肋安裝時造成地應力形變
      3. In situ stress deformation caused by the installation of control panel and side rib
      有一些生產商為處理鋁合金板版塊表面的內應力形變,尤其是控制面板選用金屬復合板時,在零部件版塊的附近加了一圈邊肋框,從生產工藝流程上是控制面板在刨槽機上按版塊壓邊規格刨槽折邊成盒狀。
      In order to deal with the internal stress and deformation on the surface of aluminum alloy plate, some manufacturers, especially when the metal composite plate is selected for the control panel, add a ring of edge rib frame near the parts plate. From the production process flow, the control panel planes the groove and folds the edge into a box shape according to the plate blank holder specification on the grooving machine.
      另一條線是將邊肋鋁型材按版塊必須規格斷開拼裝成邊肋框。隨后邊肋框裝進盒狀控制面板,用拉鉚釘將兩體固定不動。在工作中當場常常發覺因控制面板刨槽折邊有誤差,邊肋鋁型材拼裝成框有誤差,兩體相互配合常常發生并不是框小便是板折邊規格過大。為保施工期,不費料,通常強制安裝,導致表面造成安裝地應力,并不是邊肋形變便是表面受力形變。這類版塊在溫度和氣體澎漲大作下造成向外的形變狀況。
      The other line is to disconnect and assemble the edge rib aluminum profile into an edge rib frame according to the specifications of the plate. Then install the side rib frame into the box control panel and fix the two bodies with pull rivets. During the work, it is often found that there is an error in the groove folding of the control panel, and there is an error in the assembly of the edge rib aluminum profile into the frame. The two bodies often cooperate with each other. It is not the frame that urinates, but the specification of the plate folding is too large. In order to ensure the construction period and cost no materials, the installation is usually forced, resulting in the installation in-situ stress on the surface, which is either the edge rib deformation or the surface stress deformation. This kind of plate causes outward deformation under the action of temperature and gas surge.
      今天的分享就是關于鋁卷生產廠家,更多的內容小編會不斷的再此分享,更多的內容請繼續關注我們:http://www.mallhometrade.com
      Today's sharing is about aluminum coil manufacturers. More content will be shared here. Please continue to pay attention to us: http://www.mallhometrade.com